Influence of using clinical microscope as auxiliary to perform adhesive cementation of fiberglass posts: A bond strength analysis




Clinical microscope; Resin cement; Fiberglass posts; Push-out test.


This study aimed to evaluate the influence of the use of the microscope on the bond strength of fiberglass posts to dentin in the different root thirds. The crowns of sixty canines were sectioned with a diamond disc, and the roots were instrumented and filled (ProDesign Logic System 30.05 + obturation with AH Plus). Desobturation was performed with a drill corresponding to the pin diameter (DC 2, WhitePost). The roots were divided into six groups (n = 10): ACsm: Allcem and without a microscope; ACcm: Allcem and microscope; ACCsm: Allcem CORE without a microscope; ACCcm: Allcem CORE with microscope; RUsm: RelyX U200 without a microscope; RUcm: RelyX U200 with a microscope. The roots were cross-sectioned into slices of the cervical, middle and apical thirds and subjected to the bond strength test (Kratos- 0.5 mm / min / 100 Kgf). A stereomicroscope (40 x) was used to analyze the failure patterns of the samples. There was no statistically significant difference in the cervical thirds regardless of the cement used (p> 0.05). The apical third showed higher adhesion values in the group using a microscope and the self-adhesive cement (p <0.05). Conventional cement showed similar values in all root thirds (p> 0.05) and lower values compared to self-adhesive cement in the apical third (p <0.05). There was a predominance of the mixed failure pattern in the different groups and thirds. It can be concluded that the clinical microscope, the type of resin cement and the evaluated root third influenced the bond strength of fiberglass pins with the root dentin.


Amarnath, G. S., Swetha, M. U., Muddugangadhar, B. C., Sonika, R., Garg, A., & Rao, T. P. (2015). Effect of post material and length on fracture resistance of endodontically treated premolars: an in-vitro study. Journal of international oral health: JIOH, 7(7), 22.

Aktemur, T., Uzunoğlu, E., & Yılmaz, Z. (2013). Effects of dentin moisture on the push-out bond strength of a fiber post luted with different self-adhesive resin cements. Restorative dentistry & endodontics, 38(4), 234.

Aleisa, K., Al-Dwairi, Z., Alghabban, R., & Glickman, G., & Hsu, M. L. (2013). Effect of cement types and timing of cementation on the retentive bond strength of fiber posts. Journal of Dental Sciences, 7(4), 367-372.

Almeida Junior, L. J. D. S., Penha, K. J. D. S., Souza, A. F., Lula, E. C. O., Magalhães, F. C., Lima, D. M., & Firoozmand, L. M. (2017). Is there correlation between polymerization shrinkage, gap formation, and void in bulk fill composites? A μCT study. Brazilian oral research, 31.

Barjau-Escribano A., Sancho-Bru J. L., Forner-Navarro L., Rodrıguez-Cervantes P. J., Perez-Gonzalez A., & Sanchez-Marın F.T. (2006) Influence of prefabricated post material on restored teeth: Fracture strength and stress distribution Operative Dentistry 31(1) 47-54.

Barreto M. S., Rosa R. A., Seballos V. G., Machado E., Valandro L. F., Kaizer O. B., Só M. V. R., & Bier C. A. S. (2016). Effect of Intracanal Irrigants on Bond Strength of Fiber Posts Cemented With a Self-adhesive Resin Cement. Oper Dent 41(6):e159-e167.

Bitter, K., Gläser, C., Neumann, K., Blunck, U., & Frankenberger, R. (2014). Analysis of resin-dentin interface morphology and bond strength evaluation of core materials for one stage post-endodontic restorations. PLoS One, 9(2), e86294.

Bitter, K., Meyer‐Lueckel, H., Priehn, K., Kanjuparambil, J. P., Neumann, K., & Kielbassa, A. M. (2006). Effects of luting agent and thermocycling on bond strengths to root canal dentine. International endodontic journal, 39(10), 809-818.

Bouillaguet, S., Troesch, S., Wataha, J. C., Krejci, I., Meyer, J. M., & Pashley, D. H. (2003). Microtensile bond strength between adhesive cements and root canal dentin. Dental Materials, 19(3), 199-205.

Costa, J. A., Rached‐Júnior, F. A., Souza‐Gabriel, A. E., Silva‐Sousa, Y. T. C., & Sousa‐Neto, M. D. (2010). Push‐out strength of methacrylate resin‐based sealers to root canal walls. International endodontic journal, 43(8), 698-706.

Daleprane, B., Pereira, C. N., Bueno, A. C., Ferreira, R. C., Moreira, A. N., & Magalhães, C. S. (2016). Bond strength of fiber posts to the root canal: Effects of anatomic root levels and resin cements. The Journal of prosthetic dentistry, 116(3), 416-424.

De Munck, J., Vargas, M., Van Landuyt, K., Hikita, K., Lambrechts, P., & Van Meerbeek, B. (2004) Bonding of an auto-adhesive luting material to enamel and dentin. Dent Mater. 20(10):963-71.

Ekambaram, M., Yiu, C. K. Y., Matinlinna, J. P., Chang, J. W. W., Tay, F. R., & King, N. M. (2014). Effect of chlorhexidine and ethanol-wet bonding with a hydrophobic adhesive to intraradicular dentine. Journal of dentistry, 42(7), 872-882.

Elsaka, S.E. (2013) Influence of chemical surface treatments on adhesion of fiber posts to composite resin core materials. Dent Mater. May;29(5):550-8.

Faria-e-Silva, A. L., Pedrosa-Filho, C. D. F., Menezes, M. D. S., Silveira, D. M. D., & Martins, L. R. M. (2009). Effect of relining on fiber post retention to root canal. Journal of Applied Oral Science, 17(6), 600-604.

Farid, F., Rostami, K., Habibzadeh, S., & Kharazifard, M. (2018). Effect of cement type and thickness on push-out bond strength of fiber posts. Journal of dental research, dental clinics, dental prospects, 12(4), 277.

Feilzer, A. J., De Gee, A. J., & Davidson, C. L. (1993). Setting stresses in composites for two different curing modes. Dental Materials, 9(1), 2-5.

Ferrari, M., Vichi, A., Fadda, G. M., Cagidiaco, M. C., Tay, F. R., Breschi, L., Polimeni, A., & Goracci, C. (2012) A randomized controlled trial of endodontically treated and restored premolars Journal of Dental Research 91(7) 72-78.

Ferreira, R., Prado, M., de Jesus Soares, A., Zaia, A. A., & de Souza-Filho, F. J. (2015). Influence of using clinical microscope as auxiliary to perform mechanical cleaning of post space: a bond strength analysis. Journal of endodontics, 41(8), 1311-1316.

Ferreira, R. S., Andreiuolo, R. F., Mota, C. S., Dias, K. R. H. C., Miranda, M. S. (2012) Cimentação adesiva de pinos fibrorreforçados. Rev Bras Odontol. Jul-Dec;69(2):194-8.

Gaston, B. A., West, L. A., Liewehr, F. R., Fernandes, C., & Pashley, D. H. (2001). Evaluation of regional bond strength of resin cement to endodontic surfaces. Journal of Endodontics, 27(5), 321-324.

Goracci, C., Tavares, A. U., Fabianelli, A., Monticelli, F., Raffaelli, O., Cardoso, P. C., & Ferrari, M. (2004). The adhesion between fiber posts and root canal walls: comparison between microtensile and push‐out bond strength measurements. European journal of oral sciences, 112(4), 353-361.

Kadam, A., Pujar, M., & Patil, C. (2013). Evaluation of push-out bond strength of two fiber-reinforced composite posts systems using two luting cements in vitro. Journal of conservative dentistry: JCD, 16(5), 444.

Lamichhane, A., Xu, C., & Zhang, F. Q. (2014). Dental fiber-post resin base material: a review. The Journal of advanced prosthodontics, 6(1), 60.

Liu, C., Liu, H., Qian, Y.T., Zhu, S., & Zhao, S.Q. (2014) The influence of four dual-cure resin cements and surface treatment selection to bond strength of fiber post. Int J Oral Sci. Mar;6(1):56-60.

Malferrari S., Monaco C., & Scotti R. (2003) Clinical evaluation of teeth restored with quartz fiber–reinforced epoxy resin posts International Journal of Prosthodontics 16(1) 39-44).

Marques, J. D. N., Gonzalez, C. B., Silva, E. M. D., Pereira, G. D. D. S., Simão, R. A., & Prado, M. D. (2016). Análise comparativa da resistência de união de um cimento convencional e um cimento autoadesivo após diferentes tratamentos na superfície de pinos de fibra de vidro. Revista de Odontologia da UNESP, 45(2), 121-126.

Muniz, L., & Mathias, P. (2005). The influence of sodium hypochlorite and root canal sealers on post retention in different dentin regions. Operative dentistry-university of washington-, 30(4), 533.

Novais, V. R., Rodrigues, R. B., Simamoto Júnior, P. C., Lourenço, C. S., & Soares, C. J. (2016). Correlation between the mechanical properties and structural characteristics of different fiber posts systems. Brazilian dental journal, 27(1), 46-51.

Patierno, J. M., Rueggeberg, F. A., Anderson, R. W., Weller, R. N., & Pashley, D. H. (1996). Push‐out strength and SEM evaluation of resin composite bonded to internal cervical dentin. Dental Traumatology, 12(5), 227-236.

Pereira, J. R., Pamato, S., Santini, M. F., Porto, V. C., Ricci, W. A., & Só, M. V. R. (2019). Push-out bond strength of fiberglass posts cemented with adhesive and self-adhesive resin cements according to the root canal surface. The Saudi Dental Journal.

Pirani, C., Chersoni, S., Foschi, F., Piana, G., Loushine, R. J., Tay, F. R., & Prati, C. (2005). Does hybridization of intraradicular dentin really improve fiber post retention in endodontically treated teeth?. Journal of Endodontics, 31(12), 891-894.

Roberts, H. W., Leonard, D. L., Vandewalle, K. S., Cohen, M. E., & Charlton, D. G. (2004). The effect of a translucent post on resin composite depth of cure. Dental Materials, 20(7), 617-622.

Rosenstiel, S. F., Land, M. F., & Crispin, B. J. (1998). Dental luting agents: A review of the current literature. The Journal of prosthetic dentistry, 80(3), 280-301.

Sarkis-Onofre R., Jacinto C., Boscato N., Cenci M. S., & Pereira-Cenci T. (2014) Cast metal vs glass fibre posts: A randomized controlled trial with up to 3 years of follow up. Journal of Dentistry 42(5) 582-587.

Saunders, W. P., & Saunders, E. M. (1997). Conventional endodontics and the operating microscope. Dental Clinics of North America, 41(3), 415-428.

Schwartz, R. S., & Robbins, J. W. (2004). Post placement and restoration of endodontically treated teeth: a literature review. Journal of endodontics, 30(5), 289-301.

Sicuro, S. L. M., Gabardo, M. C. L., Gonzaga, C. C., Morais, N. D., Baratto-Filho, F., Nolasco, G. M. C., & Leonardi, D. P. (2016). Bond strength of self-adhesive resin cement to different root perforation materials. Journal of endodontics, 42(12), 1819-1821.

Silva, L. O., de Souza, B. P., Lima, E. M. C. X., & de Oliveira, V. M. B. (2013). Protocolos para remoção de retentores intrarradiculares de fibra de vidro: uma revisão crítica. Revista da Faculdade de Odontologia da UFBA, 43(2).

Silva, N. R. D., Rodrigues, M. D. P., Bicalho, A. A., Deus, R. A. D., Soares, P. B. F., & Soares, C. J. (2019). Effect of Magnification during Post Space Preparation on Root Cleanness and Fiber Post Bond Strength. Brazilian dental journal, 30(5), 491-497.

Silveira-Pedrosa, D. M., Martins, L. R., Sinhoreti, M. A., Correr-Sobrinho, L., Sousa-Neto, M. D., Junior, C. E., & de Carvalho, J. R. (2016). Push-out Bond Strength of Glass Fiber Posts Cemented in Weakened Roots with Different Luting Agents. The journal of contemporary dental practice.

Skupien, J. A., Sarkis-Onofre, R., Cenci, M. S., & Moraes, R. R., & Pereira-Cenci, T. A systematic review of factors associated with the retention of glass fiber posts. Braz Oral Res. 2015;29(1):S1806-83242015000100401.

Soares, C. J., Santana, F. R., Castro, C. G., Santos-Filho, P. C., Soares, P. V., Qian, F., & Armstrong, S. R. (2008). Finite element analysis and bond strength of a glass post to intraradicular dentin: comparison between microtensile and push-out tests. Dental Materials, 24(10), 1405-1411.

Tanoue, N., Koishi, Y., Atsuta, M., & Matsumura, H. (2003) Properties of dual-curable luting composites polymerized with single and dual curing modes. J Oral Rehabil. Oct;30(10):1015-21.

Tay, F. R., Loushine, R. J., Lambrechts, P., Weller, R. N., & Pashley, D. H. (2005). Geometric factors affecting dentin bonding in root canals: a theoretical modeling approach. Journal of endodontics, 31(8), 584-589.

Turp, V., Sen. D., Tuncelli, B., & Özcan, M. (2013) Adhesion of 10-MDP containing resin cements to dentin .with://

Van Landuyt, K.L., Yoshida, Y., Hirata, I., Snauwaert, J., De Munck, J., Okazaki, M., et al. (2008) Influence of the chemical structure of functional monomers on their adhesive performance. J Dent Res. Aug;87(8):757-61.

Viotti, R. G., Kasaz, A., Pena, C. E., Alexandre, R. S., Arrais, C. A., & Reis, A. F. (2009) Microtensile bond strength of new self-adhesive luting agents and conventionalmultistep systems. J Prosthet Dent. 102(5):306-12.

Wandscher V. F., Bergoli C. D., Limberger I. F., Ardenghi T. M., & Valandro L.F. (2014) Preliminary results of the survival and fracture load of roots restored with intracanal posts: Weakened vs nonweakened roots Operative Dentistry 39(5) 541-555.

Weiser, F., & Behr, M. (2015) Self-adhesive resin cements: a clinical review. J Prosthodont. Feb;24(2):100-8.



How to Cite

BARRETO, R. O.; LIMOEIRO, A. G. da S. .; NASCIMENTO, W. M.; MENDES, V.; SOUZA, C. C. .; HILGENBERG, S. P.; ARAKI, A. T. .; NAVARRO, R. S. . Influence of using clinical microscope as auxiliary to perform adhesive cementation of fiberglass posts: A bond strength analysis . Research, Society and Development, [S. l.], v. 10, n. 5, p. e0310514574, 2021. DOI: 10.33448/rsd-v10i5.14574. Disponível em: Acesso em: 27 mar. 2023.



Health Sciences